TiB2颗粒对喷射沉积Si-30AI复合材料显微组织的影响

TiB2颗粒对喷射沉积Si-30AI复合材料显微组织的影响

摘要：结合原位反应技术和喷射沉积技术制备2％ TiB2/Si-30Al铝基复合材料.应用热力学讨论TiB2颗粒的原位反应合成原理,根据原子扩散理论分析TiB2对初晶硅的改性作用.结果表明:Si-30Al中添加2％(质量分数)的TiB2能明显细化初晶硅相.在半固态二次加热过程中,TiB2颗粒能明显抑制初晶硅的粗化、长大.Abstract：An in situ reaction and spray forming technique were employed in the synthesis of 2％ TiB2/Si-30Al composite.The formation mechanism of TiB2 particulates was explained based on thermodynamic theory.The modification of the primary Si in the Si-30Al alloy was interpreted in the light of the knowledge of atomic diffusion.The experimental results show that adding 2％ TiB2 to the Si-30Al alloy can effectively refine the primary Si.Moreover,the coarsening and growth of primary Si phase in its semi-solid state was retarded effectively due to the existence of the TiB2 particulates. 作者： 甘责生[1]  张磊[2]  贝舒瑜[2]  卢毅[2]  杨滨[2] Author： GAN Gui-sheng[1]  ZHANG Lei[2]  BEI Shu-yu[2]  LU Yi[2]  YANG Bin[2] 作者单位： 北京科技大学新金属材料国家重点实验室,北京 100083;重庆理工大学材料科学与工程学院,重庆 400050北京科技大学新金属材料国家重点实验室,北京,100083 期 刊： 中国有色金属学报（英文版）   ISTICEISCI Journal： Transactions of Nonferrous Metals Society of China 年，卷(期)： 2011, 21(10) 分类号： Q946 关键词： 喷射沉积    TiB2颗粒    粗化    半固态    Keywords： spray forming    TiB2 particulate    coarsening    semi-solid state    机标分类号： TG3 TB3 机标关键词： TiB2    颗粒    喷射沉积技术    铝基复合材料    材料显微组织    microstructure    formation mechanism    初晶硅    forming technique    原位反应    in situ reaction    synthesis    knowledge    existence    质量分数    原子扩散    理论分析    加热过程    合成原理    改性作用 基金项目： the Cultivation Fund of the Key Scientific and Technical Innovation,China，Beijing Municipal Natural Science Foundation,China TiB2颗粒对喷射沉积Si-30AI复合材料显微组织的影响[期刊论文]  中国有色金属学报（英文版） --2011, 21(10)甘责生  张磊  贝舒瑜  卢毅  杨滨结合原位反应技术和喷射沉积技术制备2％ TiB2/Si-30Al铝基复合材料.应用热力学讨论TiB2颗粒的原位反应合成原理,根据原子扩散理论分析TiB2对初晶硅的改性作用.结果表明:Si-30Al中添加2％(质量分数)的TiB2能明显细化初晶硅...